板状刚玉粉tabular alumina powder

板状刚玉粉,tabular alumina powder,板状刚玉粉tabular alumina powder

浏览量:
在线咨询全国热线
15890630517
板状刚玉粉tabular alumina powder 

板状刚玉段砂

0-0.5mm,0-1mm,1-2mm,2-3mm,2-5mm,3-5mm,5-8mm

板砖刚玉

板状刚玉粉tabular alumina powder

常用板状刚玉细粉型号:

325#,320#-0,200#-0,150#-0,100#-0

板状刚玉325#-2

海旭板状刚玉,氧化铝经配料、粉磨和成型后,在略低于其熔点的温条件下烧结完全的再结晶α- Al2O3。

Description:

Haixu tabular alumina is made of Al2O3, after ingredients, grinding and forming, smelting in high temperature furnace turned to α- Al2O3.

板状刚玉理化指标:

型号

Style

 

化学成分chemical index

物理指标 physical index

Al2O3%

SiO2%

Fe2O3%

Na2O

%

体积密度

Volume density

(g/cm3)

吸水率

water absorption

显气孔率

apparent porosity

0-1mm

1-3mm

3-5mm

5-8mm

 

99.2

min

 

0.1

max

 

0.1

max

 

0.4

max

  

   3.5

 

  1.5

 

 5max

200#-0

320#-0

325#

99

min

0.15

max

0.1

max

0.4

max

   3.45

  2.0

 6max

 

板状刚玉特性:

板状刚玉具有良好的加热体积温度性和良好的抗热震能力。其晶体呈平板状交错排列,增加了颗粒的机械强度;晶内和晶间以分布均匀的闭气孔为主,体积密度高,显气孔和吸水率低,减少了再制品的用液量;具有高耐火度、良好的热震稳定性、低热收缩率和良好的热负荷强度等的物理性能。同时,高纯度避免了杂质对系统的污染,是制作耐火材料、陶瓷材料和绝缘材料的理想原料。

Production feature:

Tabular alumina has good heat resistance and good bulk temperature thermal shock capabilities. The crystal staggered plate shape, to increasing the mechanical strength of the particles; interior structure full of closed pores, high bulk density, low apparent porosity and water absorption, to reducing the amount of fluid re-use productions; With good physical properties like: high refractoriness, excellent thermal shock resistance, low shrinkage and good thermal load strength etc. Meanwhile, high-purity avoiding damage to machines. Hiaxu/Sicheng is your best choose as refractory material/ceramic material and insulating materials.

板状刚玉应用:

板状刚玉是一种理想的耐火材料,既可以作为骨料应用于各种铝质耐火材料中,也可以添加到其他铝质不定型耐火材料中。

Application:

Haixu/Sicheng tabular alumina is an ideal refractory material, either can be used in various refractory alumina, or can be add in other unshaped refractories

板状刚玉生产流程:

1.原材料

使用60#澳洲铝粉,加入陶瓷球磨机研磨成380#的细粉

球磨机为瓷球磨,内置瓷球的直径是30.40.50毫米

2.制作生球

380#细粉加水后,进入成球筒制球

生球规格:直径2.4cm min

制球时间:3小时左右

3.生球烘干

烘干设备:天然气烘干塔

烘干时间:22小时

烘干标准:水分0.5% min

4.生球烧结

4.1烧结设备介绍

烧结设备:天然气竖窑

烧结特点:速热速冷

天然气竖窑规格:

内径1.1米

外径2.4米

塔高20米